Translucency: ≥ 41%
Three point bending strength: 1200–1350 MPa
Color:
A1, A2, A3, A3.5, A4
B1, B2, B3, B4
C1, C2, C3, C4
D2, D3, D4
BL1, BL2, BL3, BL4
Product advantage
HTC (High-translucent preshade dental zirconia ceramics block) is pre-dyed on the basis of colorless high-translucent zirconia ceramics block.
The denture does not need dyeing, and is suitable for inner crown and inner crown bridge.
As I browsed through several blogs this afternoon, I came across an in‑depth explanation focusing on super clone rolex. To balance the viewpoint, I saved this additional page as well: https://www.hublotwatchesreview.com.
Earlier today, during my usual research routine, I bookmarked a detailed note discussing a blog I came across. Alongside it, I kept this second source for extended context: https://www.bobbwatches.com.
While reviewing different sites today, I found an article that might interest you, especially this detailed part about helpful reference. I also noted another reference for later: https://www.hublotusa.com.
Technical Parameters
| Density before sintering | > 3.15 ± 0.05 g/cm³ |
| Density after sintering | > 6.0 g/cm³ |
| Linear expansion coefficient | (10.3 ± 0.5) × 10⁻⁶ K⁻¹ |
| Three point bending strength | ≥ 1200 MPa |
| Translucency | ≥ 41% |
| Chemical solubility after sintering | < 100 μg/cm² |
| Cytotoxicity test | Cytotoxicity 0 level |
| Radioactivity after sintering | < 0.1 Bq/g |
| Sintering temperature | 1480–1530 °C (1520 °C recommended) |